Recently, the demand of ceramic metal halide lamp has been expanded. Therefore, the lamp with high efficiency and long lifetime are increasing and the evaluation of reliability is needed. In this paper, the degradation phenomena of ceramic metal halide lamp was studied. The lamp was tested for 3000 on/off cycles with each cycle having a duration of 20 minutes on and 20 minutes off based on the accelerated aging experiment based on "Reliability Standards RS C 0085". As result, the corrosion of arc tube and leak was appeared from reaction between inner wall of PCA and chemical elements, and distortion of electrode was resulted from difference of thermal expansion between arc tube of PCA and electrode. Also, the efficiency of lamp was decreased by the change of inner pressure, operation temperature, and driving voltage from wall blackening.