In this study, KTN heterolayer thin films were fabricated by alternately stacking films of K(Ta0.70Nb0.30)O3 and K(Ta0.55Nb0.45)O3 synthesized using the sol-gel method. The sintering temperature and time were 750℃ and 1 hour, respectively. All specimens exhibited a polycrystalline pseudo-cubic crystal structure, with a lattice constant of approximately 0.398 nm. The average grain size was around 130~150 nm, indicating relatively uniform sizes regardless of the number of coatings. The average thickness of a single-coated film was approximately 70 nm. The phase transition temperature of the KTN heterolayer films was found to be approximately 8~12℃. Moreover, the 6-coated KTN heterolayer film displayed an excellent dielectric constant of about 11,000. As the number of coatings increased, and consequently the film thickness, the remanent polarization increased, while the coercive field decreased. The 6-coated KTN heterolayer film exhibited a remanent polarization and coercive field of 11.4 μC/cm2 and 69.3 kV/cm at room temperature, respectively. ΔT showed the highest value at a temperature slightly above the Curie temperature, and for the 6-coated KTN heterolayer film, the ΔT and ΔT/ΔE were approximately 1.93 K and 0.128×10-6 K·m/V around 40℃, respectively.
In this study, double layer KTN/STO thin films were fabricated on Pt/Ti/SiO2/Si substrate, their structural and electrical properties were measured according with the number of STO coatings, and their applicability to microwave materials was investigated. The average grain size was about 80~90 nm, the average thickness of the 6-coated KTN thin film was about 320 nm, and the average thickness of the STO thin film coated once was about 45~50 nm. The dielectric constant decreased with increasing frequency, and as the number of STO coatings increased, the rate of change of the dielectric constant with the applied electric field decreased. The tunability of the KTN thin film showed a maximum value of 19.8% at 3 V. The figure of merit of the KTN/1STO thin film was 9.8 at 3 V.
First
Prev