In this study, SiO₂ 20 phr, ATH 70 phr, and platinum flame retardant were mixed with raw silicone rubber and -10 kV was applied to measure electrostatic charge attenuation voltage, surface resistance, and volume resistance, and the following conclusions were obtained. When the platinum flame retardant was 0 phr, the humidity 74.6% and the temperature was 21.8℃, the potential was half-reduced to 0.63 kV, 0.57 kV, and 0.44 kV when the applied voltage was changed from -10 kV to -8 kV, and the time halved to 50% was increased to 2.40 seconds, 2.47 seconds, and 2.61 seconds. It was confirmed that as the platinum flame retardant increased from 0.1 to 0.3 phr, the potential half-reduced to 0.67 kV, 0.60 kV, and 0.595 kV decreased, and the charge potential attenuation time half-reduced to 50% decreased to 3.44 seconds, 1.78 seconds, and 1.60 seconds. It was confirmed that the surface resistance increased as the humidity decreased, and the volume resistance decreased as the platinum flame retardant increased.

Porcelain insulators have been used mainly for power line fixing and electrical insulation in transmission towers. Porcelain insulators have generally a 30 years desired life, but over 50% exceed their life expectancy. Since the damage to porcelain insulators is usually accompanied by enormous loss of human resource material, their efficient maintenance has emerged as an important issue. In this regard, this study applied a frequency response function (FRF) for integrity assessment of the insulator. The characteristics of the FRF according to damage types were identified and analyzed by the change in natural frequencies, curve shape, attenuation, and Nyquist diagram stability. The results showed significant differences in the FRF according to damage types, which can be used as basic data for the effective integrity assessment of porcelain insulators.