Randomly patterned and wet chemical etching processes were used to treat anti-glare of display cover glasses. The surface and optical properties of grain size and surface morphology controlled by randomly patterned etching and wet chemical solution etching were investigated. The surface morphology and roughness of the etched samples were examined using a spectrophotometer and a portable surface roughness (Ra) measuring instrument, respectively. The gloss caused by reflection from the glass surface was measured at 60° using a gloss meter. The surface of the sample etched by the doctor-blade process was more uniform than that obtained from a screen pattern etching process at gel state etching process of the first step. The surface roughness obtained from the randomly patterned etching process depended greatly on the mesh size, which in turn affected the grain size and pattern formation. The surface morphology and gloss obtained by the etching process in the second step depended primarily on the mesh size of the gel state etching process of the first step. In our experimental range, the gloss increased on decreasing the grain size at a lower mesh size for the first step process and for longer reaction times for the second step process.

To provide the clear images from the direct light on electrical board and display devices, anti glare treatment of display cover glass is needed. In this study, the effects of surface treatment temperature, concentration, and etching solution coating thickness of the gel phase on optical elements control such as gloss, haze of reflected light and transmittance, were investigated. Cover glasses were treated at different coating thickness and additive concentration. The optical properties were examined using spectrophotometer, gloss and haze meter. The surface morphology and roughness were measured by the optical microscope and Ra measuring instrument. The etching rate and surface morphologies were dramatically affected by the concentration of acid additive in the viscous gel because of re-crystallization of components in the etching solution, hydrogel formation and coagulant after coating on glass substrate. In our experimental range, cover glass which is surface-treated with various optical properties as well as the morphology uniformity was obtained; in particular, optical properties could be controlled by etching solution coating thickness of the gel phase and the concentration of additive. The gloss was depended on the surface roughness and it showed the linear relationship between optical transmittance and haze of reflected light, respectively.