Randomly patterned and wet chemical etching processes were used to treat anti-glare of display cover glasses. The surface and optical properties of grain size and surface morphology controlled by randomly patterned etching and wet chemical solution etching were investigated. The surface morphology and roughness of the etched samples were examined using a spectrophotometer and a portable surface roughness (Ra) measuring instrument, respectively. The gloss caused by reflection from the glass surface was measured at 60° using a gloss meter. The surface of the sample etched by the doctor-blade process was more uniform than that obtained from a screen pattern etching process at gel state etching process of the first step. The surface roughness obtained from the randomly patterned etching process depended greatly on the mesh size, which in turn affected the grain size and pattern formation. The surface morphology and gloss obtained by the etching process in the second step depended primarily on the mesh size of the gel state etching process of the first step. In our experimental range, the gloss increased on decreasing the grain size at a lower mesh size for the first step process and for longer reaction times for the second step process.