Transparent color coating films were fabricated on a glass substrate by using sol-gel hybrid binder and organic dye. Sol-gel hybrid binder coating film fabricated with PTMS of 0.03 mole showed a very high pencil hardness of 9 H. As the withdrawal speed increased from 1.0 mm/s to 5.0 mm/sec, The yellowness (b*) of coating glass also gradually increased. The transmittance of yellow color coating glass was 82.6% and the haze of coating glass was 0.35%. Red and blue color coating glasses also showed the high transmittance of 62.4% and 80.6% respectively. The surface hardness of color coating films was 6 H.