CIGS is one of thin film solar cell and has been studied so much, because of the possibility of low price and high efficiency. Until now, co-evaporation and sputtering were typical method to prepare CIGS absorption layer, and a few company commercialized solar cell by these method. However,non-vacuum process which has been studied for long time has not been progressed, though the merit of low price. Especially, aerosol deposition method has not been reported, because it is difficult to prepare a large quantity of various CIGS powder. In this study, CIGS powder was synthesized by mechanochemical method and CIGS absorption layer was deposited by aerosol deposition method. The thickness of the CIGS layer was controlled by the number of deposition and the surface roughness of it was affected by the amount of flow gas. And, also, I-V curve of it appeared metallic property in the case of ‘as deposition’. After heat treatment in Se-rich atmosphere, the electrical property of it changed to a semiconductor. CdS and transparent conduction layer were formed by a typical method on it for solar cell. The efficiency of cell was appeared 0.19%. Though the efficiency was low because of the disharmony in the after-process, it was conformed that CIGS solar cell could be prepared by aerosol deposition.