In this study, lead-free (Na0.465K0.465Bi0.07)(Nb0.93Ti0.07)O3-0.08MnO2 ceramics were fabricated by conventional mixed oxide method. Structural and electrical properties of lead-free (Na0.465K0.465Bi0.07)(Nb0.93Ti0.07)O3-0.08MnO2 ceramics with the variation of sintering temperature were investigated. As results of x-ray diffraction analysis, all specimens showed a typical polycrystalline perovskite structure without presence of the second phase. Sintered density increased with an increases of sintering temperature and the specimen sintered at 1,020℃ showed the maximum value of 4.5 g/cm3. The average grain size of the (Na0.465K0.465Bi0.07)(Nb0.93Ti0.07)O3-0.08MnO2 specimen sintered at 1,020℃ is about 0.83 μm. Electromechanical coupling factor, relative dielectric constant and dielectric loss of (Na0.465K0.465Bi0.07)(Nb0.93Ti0.07)O3-0.08MnO2 specimens sintered at 1,020℃ were 0.252, 741 and 0.043% respectively.