Recently, remote phosphor is reported for white LED enhancing of phosphor efficiency compared with conventional phosphor-based W-LED. In this study, Remote phosphor was produced by screen printing coating on glass substrate with phosphor contents rated paste and heat treatment. The paste consists of phosphor, lowest softening glass frit and organic binders. Remote phosphor can be well controlled by varying the phosphor content rated paste. After mounting remote phosphor on top of blue LED chip, CCT, CRI, and luminance efficiency were measured. The measurement results showed that CCT, CRI. and luminance efficiency were 6,645, 68, and 1,161 n/W in phosphor 80 wt.% remote phosphor sintered at 600℃.

We developed a package of remote phosphor structure having blue LED chips and phosphors physically separated, and the characteristics were evaluated according to different classifications of phosphor coatings. Remote phosphor was produced by screen printing coating on glass substrate with phosphor content rated paste and heat treatment. After mounting Remote phosphor, which has been classified according to number of coatings, on top of blue LED chips, luminous flux, luminous efficacy, CCT and CRI were measured. The measurement results showed the most suitable characteristics of white LED package as a general light source when the content rate of phosphor in Remote phosphor was 80 wt.% with 3 layers of coatings and thickness over 12 μm.