La_0.7Sr_0.3-xMg_xMnO₃ (LSMMO) (x=0.05~0.20) specimens are fabricated by a solid phase sintering method, and the sintering temperature and time are 1,300℃ and 2 hours, respectively. The dependence of the crystalline structure according to the amount of Mg²⁺ contents is not observed, and all specimens show a polycrystalline rhombohedral crystal structure, the X-ray diffraction (110) peaks move to the high angle side with increasing the amount of Mg²⁺ contents. LSMMO specimens exhibit a granule-shaped microstructure with an average grain size of 1 μm or less. Resistivity gradually decrease as the amount of Mg²⁺ contents increased. And in the La_0.7Sr_0.1Mg_0.2MnO₃ specimen, resistivity and B_25/65-value are 36.7 Ω-cm and 394 K at room temperature, respectively. LSMMO specimens show a variable-range hopping (VRH) electrical conduction mechanism, and the negative temperature of coefficient of resistance (NTCR) is approximately 0.37~0.38%/℃.