Wrinkle patterns were fabricated on styrene-butadiene-styrene (SBS) block copolymer substrates using ion-beam (IB) irradiation with various intensities. The wavelength of the wrinkle pattern increased as the IB intensity was increased from 800 to 1,600 eV. IB irradiation-induced changes in the surface properties that were confirmed via physicochemical surface analyses. X-ray photoelectron spectroscopy analysis revealed chemical surface reformation due to the IB irradiation, resulting in C-O/C=O bonds after IB irradiation that were not reported before. These results indicate that the surface chemical modification caused by IB irradiation is strongly related to the surface modulus, which is important when fabricating wrinkle patterns. Furthermore, a strong IB irradiation induced a strong compressive strain; thus the size of the wrinkle pattern was increased.

The alignment characteristics of liquid crystal (LC) molecules on a solution-derived lanthanum zinc oxide (LZO) film under ion-beam irradiation were demonstrated. Using the solution process, an LZO film was fabricated on the glass substrate and cured at 100℃. Afterwards, ion-beam irradiation was performed following the LC alignment method. Using this film, an LC cell was fabricated and the characteristics of the LC alignment were verified. Cross polarizing microscopy and the crystal rotation method were used to investigate the alignment state of the LC molecules on the LZO films. Furthermore, field emission scanning electron microscopy and X-ray photoelectron spectroscopy were used to explore the effect of the ion-beam irradiation on the LZO film. Through these, it was confirmed that the ion-beam irradiation induced surface modification, which demonstrated anisotropic physical and chemical surface characteristics. Due to this, uniform LC alignment was achieved. Finally, the residual DC and anchoring energy of the LC cell based on the LZO films were measured using a capacitance-voltage curve.