We investigated the effect of a post-annealing process using ultraviolet (UV) light on the electrical properties of solution-processed InZnO (IZO) thin-film transistors (TFTs). UV light was irradiated on IZO TFTs for different time periods of 0s, 30s, and 90s. We measured transfer and retention stability curves to evaluate the performance of the fabricated TFTs. In addition, we measured height, amplitude, and phase AFM images to analyze changes in the surface and morphology of the devices. AFM measurements were performed by setting the drive amplitude of the cantilever tip to 47.9 mV in tapping mode, then dividing the device surface into 500 nm × 500 nm. In the case of IZO TFT irradiated with UV for 30s, the electron mobility and Ion/Ioff ratio were improved, the threshold voltage was reduced by approximately 2 V, and the subthreshold swing also decreased form 1.34 V/dec to 1.11 V/dec.

We investigated the effect of different thin-film thicknesses (25, 30, and 40 nm) on the electrical performance of solution-processed indium-zinc-oxide (IZO) thin-film transistors (TFTs). The structural properties of the IZO thin films were investigated by atomic force microscopy (AFM). AFM images revealed that the IZO thin films with thicknesses of 25 and 40 nm exhibit an uneven distribution of grains, which deforms the thin film and degrades the performance of the IZO TFT. Further, the IZO thin film with a thickness of 30 nm exhibits a homogeneous and smooth surface with a low RMS roughness of 1.88 nm. The IZO TFTs with the 30-nm-thick IZO film exhibit excellent results, with a field-effect mobility of 3.0(±0.2) cm²/Vs, high Ion/Ioff ratio of 1.1×10⁷, threshold voltage of 0.4(±0.1) V, and subthreshold swing of 0.7(±0.01) V/dec. The optimization of oxide semiconductor thickness through analysis of the surface morphologies can thus contribute to the development of oxide TFT manufacturing technology.