To study encapsulation method for large-area organic light emitting diodes (OLEDs), red emitting OLEDs were fabricated, on which Alq3 as organic buffer layer and LiF and Al as inorganic protective layers were deposited to protect the damage of OLED by epoxy. And then the OLEDs were attached to flat glass by printing method using epoxy. The basic structure of OLED doped with rubrene of 1 vol.% as emitting layer is ITO(150 ㎚)/2-TNATA(50 ㎚)/α-NPD(30 ㎚)/Alq3:Rubrene(30 ㎚)/Alq3(30 ㎚)/LiF(0.7 ㎚)/Al(100 ㎚). In case of depositing Alq3, LiF and Al and then attaching of flat glass onto OLED, current density, luminance, efficiency and driving voltage were not changed and lifetime was increased according to thickness of Al as inorganic protective layers. The lifetime of OLED/Alq3/LiF/Al_4/glass structure was 139 hours increased by 15.8 times more than bare OLED of 8.8 hours and 1.6 times more than edge sealed OLED of 54.5 hours.

To study encapsulation method for large-area organic light emitting diodes (OLEDs), red emitting OLEDs were fabricated, on which LiF and Al were deposited as inorganic protective films. And then the OLED was attached to flat glass by printing method using epoxy. In case of direct coating of epoxy onto OLED by printing method, luminance and current efficiency were remarkably decreased because of the damage to the OLED by epoxy. In case of depositing LiF and Al as inorganic protective films and then coating of epoxy onto OLED, luminance and current efficiency were not changed. OLED lifetime was more increased through inorganic protective films between OLED and flat glass than that without any encapsulation (8.8 h), i.e., 47 (LiF/Al/epoxy/glass), 62 (LiF/Al/LiF/epoxy/glass), and 84 h (LiF/Al/Al/epoxy/glass). The characteristics of OLED encapsulated with inorganic protective films (attached to flat glass) showed the possibility of application of protective films.