In order to develop an electrical insulation material for gas GIS (insulation switch gear) spacer, 4 types of epoxy/micro-alumina (40, 50, 60, 70 wt%) composites and 9 types of epoxy/nano-alumina (1, 3, 5 g)/micro-alumina (40, 50, 60, 70 wt%) composites were prepared and tensile test was carried out. In here, nano-alumina was previously surface-treated with GDE (glycerol diglycidyl ether). As micro-alumina and GDE-treated nano-alumina contents increased, tensile strength increased and the highest value was shown in the system with 3 g GDE-treated nano-alumina.

In this work, the complex permittivity of epoxy resins is measured. Epoxy resins, epoxy with micro size fillers and epoxy with micro+nano alumina composites have been evaluated for dielectric properties according to frequency variation. The dielectric spectroscopy measurement and analyses are carried out in the frequency range of 10^-2 Hz to 1MHz and constant to room temperature. The results of dielectric loss suggest that significant improvement in the electrical performance can be expected by using samples containing nano and micro fillers mixture when compared to materials containing only microfillers. As the result, we verified the specific characteristics of dielectric permittivity and dielectric loss namely, relative permittivity become low with improving dispersibility of nano+micro mixture composites and become rise with agglomerate of nano particles.