The low-temperature deposition of BaNi_(2-x)Co_xFe₁₆O₂₇ thin films with a Ba hexaferrite structure for electromagnetic shielding was studied. The BaNi_(2-x)Co_xFe₁₆O₂₇ thin films produced through the spin spray process were suitable for thin film deposition on a flexible substrate because it crystallized well at low temperature below 90℃. The change in shielding characteristics depending on the Co content of the BaNi_(2-x)Co_xFe₁₆O₂₇ thin film was investigated, and excellent shielding characteristics with S21 of -1 dB were obtained in a wide frequency range of 26~40 GHz when the Co content was 0.4 or more. The purpose of this study is to analyze changes in shielding properties caused by change in Co content in relation to phase changes in BaNi_(2-x)Co_xFe₁₆O₂₇ and obtain basic data for developing excellent flexible electromagnetic wave shielding materials.

In this study, we intended to achieve both antibacterial properties and electromagnetic shielding using the Al-doped ZnO (AZO) films. FTS (Facial Target Sputtering) magnetron sputtering was used for the AZO thin films instead of the conventional RF sputtering because the FTS sputtering could avoid the damage for the plasma as well as fabrication of thin films with a high quality. The 300-nm thick AZO thin films grown on glass substrate showed a resistivity of about 7 × 10-4 Ω-cm and a transmittance of about 90% at a wavelength of 550 nm. AZO thin films were investigated for the electromagnetic shielding effectiveness measured by 2-port network method at 1.5 ~ 3 GHz. The AZO (300 nm)/glass films showed an EMI shielding effectiveness of approximately 27 dB. An antibacterial effect was measured by the film attachment method (JIS Z 2801). The percent reductions of bacteria by AZO films were 99.99668% and 99.99999% against Staphylococcus aureus and Escherichia coli, respectively.