AGZO thin films were deposited on glass substrates using RF magnetron sputtering system under Ar flow rates, and their structural, electrical, and optical properties were analyzed systematically. As a result of the XRD pattern, the peak of the (002) (2θ≈33.7˚) orientation was observed, and it was found to have a hexagonal wurtzite structure. The sheet resistance of Ar 5 sccm was 3.073×10² Ω/sq and showed the best electrical properties because of the improvement of mobility due to the increase of the grain size and the variation of RMS roughness. In addition, the average transmittance was more than 90% for all samples, which demonstrated good optical properties. It is expected that the TCO characteristics can be improved by controlling Ar flow rates, and this will increase the efficiency of photoelectronic devices such as OLED and solar cells.